不銹鋼化學(xué)成分表
發(fā)布時(shí)間：2009/8/27
組織類型
| 序號
| 牌號
| 化學(xué)成分，%
|
碳
| 硅
| 錳
| 磷
| 硫
| 鎳
| 鉻
| 鉬
| 其他
| 國外牌號
|
奧氏體型
| 1
| 0Cr18Ni9
| 0.07
| 1.00
| 2.00
| 0.035
| 0.030
| 8.00-11.00
| 17.00-19.00
| -
| -
| TP304
|
2
| 1Cr19Ni9
| 0.04-0.10
| 1.00
| 2.00
| 0.035
| 0.030
| 8.00-11.00
| 18.00-20.00
| -
| -
| TP302
|
3
| 00Cr19Ni9
| 0.030
| 1.00
| 2.00
| 0.035
| 0.030
| 8.00-12.00
| 18.00-20.00
| -
| -
| TP304L
|
4
| 2Cr23Ni13
| 0.20
| 1.00
| 2.00
| 0.035
| 0.030
| 12.00-15.00
| 22.00-24.00
|
|
| -
|
5
| 0Cr23Ni13
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 12.00-15.00
| 22.00-24.00
| -
| -
| -
|
6
| 2Cr25Ni20
| 0.25
| 1.00
| 2.00
| 0.035
| 0.030
| 19.00-22.00
| 24.00-26.00
| -
| -
| -
|
7
| 0Cr25Ni20
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 19.00-22.00
| 24.00-26.00
| -
| -
| TP310S
|
8
| 0Cr17Ni12Mo2
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 10.00-14.00
| 16.00-18.50
| 2.00-3.00
| -
| TP316
|
9
| 1Cr17Ni12Mo2
| 0.04-0.10
| <0.75
| 2.00
| 0.030
| 0.030
| 11.00-14.00
| 16.00-18.00
| 2.00-3.00
| -
| -
|
10
| 00Cr17Ni14Mo2
| 0.030
| 1.00
| 2.00
| 0.035
| 0.030
| 12.00-15.00
| 16.00-18.00
| 2.00-3.00
| -
| TP316L
|
11
| 0Cr19Ni13Mo3
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 11.00-15.00
| 18.00-20.00
| 3.00-4.00
| -
| TP317
|
12
| 00Cr19Ni13Mo3
| 0.030
| 1.00
| 2.00
| 0.035
| 0.030
| 11.00-15.00
| 18.00-20.00
| 3.00-4.00
| -
| TP317L
|
13
| 1Cr18Ni9Ti
| 0.12
| 1.00
| 2.00
| 0.035
| 0.030
| 8.00-11.00
| 17.00-19.00
| -
| Ti? 5×(C%-0.02)~0.80
| TP321H
|
14
| 0Cr18Ni10Ti
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 9.00-12.00
| 17.00-19.00
| -
| Ti? >5×C%
| TP321
|
15
| 1Cr18Ni11Ti
| 0.04-0.10
| <0.75
| 2.00
| 0.030
| 0.030
| 9.00-13.00
| 17.00-20.00
| -
| Ti? 4×C%~0.60
| -
|
16
| 0Cr18Ni11Nb
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 9.00-13.00
| 17.00-19.00
| -
| Nb? ≥10×C%
| -
|
17
| 1Cr19Ni11Nb
| 0.04-0.10
| 1.00
| 2.00
| 0.035
| 0.030
| 9.00-13.00
| 17.00-20.00
| -
| Na+Ta≥8×C%~1.00
| -
|
18
| 0Cr18Ni13Si4
| 0.08
| 3.00-5.00
| 2.00
| 0.035
| 0.030
| 11.50-15.00
| 15.00-20.00
| -
| -
| -
|
19
| 0Cr18Ni12Mo2Ti
| 0.08
| 1.00
| 2.00
| 0.035
| 0.030
| 11.00-14.00
| 16.00-19.00
| 1.50-2.50
| Ti? 5×C%~0.70
| -
|
20
| 1Cr18Ni12Mo2Ti
| 0.12
| 1.00
| 2.00
| 0.035
| 0.030
| 11.00-14.00
| 16.00-19.00
| 1.50-2.50
| Ti? 5×(C%-0.02)~0.80
| -
|
21
| 1Cr18Ni12Mo3Ti
| 0.12
| 1.00
| 2.00
| 0.035
| 0.030
| 11.00-14.00
| 16.00-19.00
| 2.50-3.50
| Ti ?5×(C%-0.02)~0.80
| -
|